降温变面轧制AZ31镁合金组织性能演化

时间:2018-07-10 16:32来源:毕业论文
通过对制备Mg-3Al-1Zn合金的加工工艺进行改进探索,形成降温变面轧制工艺方式,以此来加强Mg-3Al-1Zn合金的综合机械性能。试验过程当中我们通过金相显微镜、透射电子显微镜和衍射仪等

摘要镁合金是目前生活及生产应用用最为广泛的轻质结构材料。镁合金因其良好的铸造性、抗腐蚀性及尺寸稳定性高等特点在航天领域、汽车、国防事业、电子等产业中具有广阔的应用前景。因为现有工业所加工的镁合金普遍存在强度低、塑性差等不足,因而本文通过对制备Mg-3Al-1Zn合金的加工工艺进行改进探索,形成降温变面轧制工艺方式,以此来加强Mg-3Al-1Zn合金的综合机械性能。试验过程当中我们通过金相显微镜、透射电子显微镜和衍射仪等察看降温变面轧制后Mg-3Al-1Zn合金的微观构造和常规变面轧制后的Mg-3Al-1Zn合金对比发现微观组织发生很大改变,动态再结晶不足,晶粒没法细化且晶粒不能均匀分布,孪生大量产生。此外,通过单轴拉伸力学性能实验所测得的数据和微观组织情况结合分析发现降温变面轧制Mg-3Al-1Zn合金的强度增加,塑性升高且延伸率提高。25580
关键词  Mg-3Al-1Zn合金  动态再结晶 晶粒细化 孪晶 力学性能
重庆时时彩的规律设计说明书外文摘要
Title   Microstructure and mechanical properties of Variable- plane -rolled AZ31 magnesium alloy under decreasing temperture
Abstract
Magnesium alloy is a light structural material what used widely in life and  production. Because of its good casting properties, corrosion resistance and dimensional stability, magnesium alloy has wide application in the field of  aerospace, automotive, defense, electronics and other industries. But magnesium alloys made by traditional plastic machining have many disadvantages, In this paper, AZ31 magnesium alloys were processed by variable-plane rolling, cooling variable-plane rolling and variable-plane sheet rolling, in order to improve the mechanical properties of magnesium alloys. 源自:六W维L论*文;网.加7位QQ3249'114 重庆时时彩的规律 www.mamitama.com
In this lab, from the evolved microstructures that were observed by optical microscopy, transmission electron microscopy (TEM) and X-ray diffraction (XRD).  we can find that the microstructures of variable-plane-rolled AZ31 magnesium alloy are changed obviously. Dynamic recrystallization occurs during deformation. Grain size is refined and homogeneous. The number of twins is increasing. In addition, the tensile strength of AZ31 magnesium alloy was significantly increased through the uniaxial tension and compression, the ductility and the elongation rate was also improved. And through the experimental contrast, it can be seen that the deformation temperature is decreased, the dynamic recrystallization is not enough, and the grain size is blocked.
Keywords  AZ31 magnesium alloy Dynamic recrystallization Gain refinement  Twin   Mechanical properties
目   次
1 绪论    1
1.1 课题研究背景    1
1.1.1镁合金介绍    1
1.1.2 镁合金的分类及应用    1
1.1.3 镁合金的轧制工艺及研究现状    1
1.2 力学性能的影响因素    2
1.2.1 晶粒细化对镁合金力学性能的影响    2
1.2.2 织构对镁合金力学性能的影响    3
1.2.3 动态再结晶对镁合金力学性能的影响    3
1.3本课题的研究目的、内容及意义    3
2 实验方法    5
2.1 镁合金的制备    5
2.1.1 实验材料    5
2.1.2 降温变面轧制AZ31镁合金    5
2.2 力学性能测试    7
2.3 微观组织分析    8
2.3.1 金相组织观察    8
2.3.2 X射线衍射分析    9 本文来源:http://www.mamitama.com/a/www.aqdgxww.com/

重庆时时彩的规律 www.mamitama.com,由于体积小、功耗低,这套系统可轻易部署在机器人、无人机等智能设备中,为智能视频在现实环境中的应用,带来更加灵活的解决方案,助力智慧城市建设。(陈立希新华社专特稿)

源自:六W维L论*文;网.加7位QQ3249'114 重庆时时彩的规律 www.mamitama.com


2.3.3 扫描电子显微镜分析    9
2.3.4 透射电子显微镜分析    9
3 实验结果    10
3.1降温变面轧制AZ31镁合金    10 降温变面轧制AZ31镁合金组织性能演化:/a/cailiao/20180710/19430.html
------分隔线----------------------------
推荐内容
小说 小说 小说 小说 小说 小说
小说 小说 小说 小说 小说 小说
小说 小说 小说 小说 小说 小说
陕西11选5今日走势 广西快乐十分开奖直播 福彩3d开奖号 排列3 广西快三规律
江西时时彩开奖走势图 排列三字谜 广西快乐双彩最新开奖 北京赛车软件 极速时时彩官方网